10 Pins Zirconia Connector Cover with Holes
- Brand Name
- 3X ceramic parts
- Material Type
- zirconia ceramic
- Forming Way
- isostatic pressing
- MOQ
- 5 pcs
- Specification
- custom make
- Density
- 6.0g/cm3
- Surface finish
- cnc machined
- Application
- connector cover
- Main Property
- high strength
- Machining Way
- CNC machining
- Max working temperature
- 1050 ℃
- Thermal Conductivity
- 2-2.2 W/ (m.k )
- Compressive Strength
- 2000 Mpa
- Flexural Strength
- 950 Mpa
- Tolerance
- 0.001mm
- Delivery Time
- 15 days around
- Shipping Way
- by express
Machined 10 Pins Zirconia Connector Cover with Holes
The 10 pins zirconia connector cover blank are formed by isostatic pressing , it with higher density 6.0g / cm3 . The holes and steps are manufactured on CNC high precision machining machine . The machining tolerance we could even achieve as high as 0.001mm . Zirconia Ceramic machined parts is belong to ceramic structure custom machined parts . It used as connector cover as it is high strength , corrosion resistant , electrical insulating and more wearable .
Drawings of zirconia connector cover with holes :
Here is the composition sheet of zirconia ceramic material :
| Physical - Chemical Inspection Sheet of Products | |||
| Type: FMY-SB-3.0, Lot No : 14-06033 | |||
| Inspection Result , PASS | |||
| NO | ITEM | VALUE | METHOD |
| 1 | ZrO2(HfO2)% | >94.3±0.1 | - |
| 2 | Y2O3 % | 5.4±0.2 | JY-38IIAES |
| 3 | Fe2O3% | <0.0030 | YB/T568.2-2008 |
| 4 | Na2O3% | <0.0400 | YB/T568.5-2008 |
| 5 | SiO2% | <0.0100 | YB/T568.3-2008 |
| 6 | TiO2% | <0.001 | YB/T568.6-2008 |
| 7 | Cao% | - | - |
| 8 | MgO% | - | - |
| 9 | AL2O3% | < 0.25 | YB/T568.4-2008 |
| 10 | CeO2% | - | - |
| 11 | CI% | <0.02 | GB/T9729-2007 |
| 12 | Lg Loss % | 3.23 | 1000°C, 1h |
| 13 | H2O% | 0.31 | 110°C, 1h |
| 14 | Sbet M2/G | 10.6 | SSA-3600比表面仪 |
| 15 | D50um | 1.444 | MS2000粒度仪 |
| 16 | TD G/ML | - | - |