Ceramic Centering Pin
- Brand Name
- 3X Ceramic Parts
- Material Type
- blue zircoinia
- Forming Way
- isostatic pressing
- MOQ
- 5 pcs
- Specification
- custom make
- Hardness
- 1200HV
- Density
- 6.0g/cm3
- Surface finish
- polished
- Application
- welding technology
- Main Property
- high strength
- Machining Way
- grinding
- Max working temperature
- 1000℃
- Thermal Conductivity
- 3 W/( m.k)
- Compressive Strength
- 2000Mpa
- Delivery Time
- 15 days around
- Shipping Way
- by express
Long Service Life Blue Zirconia Ceamic Centering Pin
Characteristics of blue zirconia ceramic centering pin :
Refractory with Long service life, High Polished Surface , Superior Mechanical Strength, Anti-high Corrosion and Wear Resistance, Good Insulation Performance ,High Temperature and Pressure Resistance
High Purity Zirconia and Alumina Ceramic Materials ; High hardness, long service life, not easy to break and wear resistance; non-conductive, anti-static, ceramic material itself with the insulation of electricity and magnetism properties, corrosion resistance, high temperature resistance, can be applied to a specific environment, such as acid alkali resistance
Ceramic Centering Pins performance parameters:
| Attribute | Zirconia | Alumina | ZTA |
| Density | 5.9-6.05g/cm3 | 3.6-3.8g/cm3 | 4.8g/cm3 |
| Hardness(HRC) | 88-90 | 80-86 | 86 |
| Fracture Toughness | 10MPa.m½ | 4MPa.m½ | - |
| Compressive Strength | 2000MPa | 1500MPa | 1700MPa |
| CTE | 10.5ppm/ºC | 7.15-7.67ppm/ºC | 9.1ppm/ºC |
| Maximum Operating Temperature |
1350ºC | 1700ºC | 1350ºC |
| Thermal Conductivity(24ºC) | 2W/m.k | 18-28W/m.k | - |
| Flexural Strength (24ºC) | 950MPa | 300MPa | 600MPa |
| Water Absorption(%) | 0 | 0 |